Super duplex Stainless Steel grades 2507

2507 is one of a group of "super duplex" grades, combining high strength with exceptional corrosion resistance.

2507 is very highly resistant to general corrosion and to pitting and crevice corrosion in high chloride, hot environments. Its duplex structure also results in excellent resistance to stress corrosion cracking.

Stainless Steel Chemical plants and temperature control image credit: http://www.tempcoblog.com/4688/chemical-plants-and-temperature-control/

Like other duplex (ferritic/austenitic) grades the super duplex grades are not suitable for high or low temperature service. 2507 is not recommended for temperatures below -50°C or above +300°C, because of reduced toughness outside this range.

The high strength favours applications in pressure vessels and for marine and other shafts

Corrosion Resistance

2507 has excellent general corrosion resistance, superior to virtually all other stainless steels. It has high resistance to intergranular corrosion and very high resistance to stress corrosion cracking in both chloride and sulphide environments.

A PRE of least 40 indicates that the material has good pitting and crevice corrosion resistance to warm sea water and other high chloride environments; it is rated as more resistant than grade 904L and approximating that of the 6% Molybdenum "super austenitic" grades.

2507 is the grade of choice for severe high temperature marine environments and for chemical and petrochemical processing, even including some solutions of strong acids.

Consult Atlas Technical Assistance for specific environmental recommendations.

Read more:

Stainless Steel Grade 2304 duplex (Ferritic/Austenitic)

Stainless Steel 304 vs 316 Stainless Steel

Stainless Steel Grade 630 Composition Specification (%)

Heat Resistance

Although super duplex grades have good high temperature oxidation resistance, like other duplex stainless steels they suffer from embrittlement if held for even short times at temperatures above 300°C. If grade 2507 becomes embrittled this can only be rectified by a full solution annealing treatment.

Heat Treatment

Solution Treatment (Annealing)

Heat to 1040 - 1120°C and cool rapidly in air or by water quenching.

Duplex and super duplex grades cannot be hardened by thermal treatment.

Welding

2507 is weldable by standard methods, without pre-heat. Consumables over-alloyed with nitrogen and nickel are generally recommended such as those with ISO designation “25 9 4 L N”. TIG (GTAW), MIG (GMAW) and all positional manual (MMAW) electrodes are available. Heat input should be within the range 0.5 – 1.5kJ/mm. Post weld annealing is essential following autogenous welding, but not otherwise. Nickel-based consumables (eg Alloy C22) can also be used to give higher corrosion resisting welds. As for other duplex stainless steels the coefficient of thermal expansion of 2507 is lower than for austenitic grades, reducing distortion and residual stresses.

Fabrication

2507 is a high strength steel, so high forming forces will be required and high spring-back should be anticipated. The ductility of the grade is quite adequate for most operations, but heavy deformation, such as cold forging, is not possible. If more than about 20% cold work is carried out an intermediate solution anneal is required. Hot forging can be carried out in the temperature range 1200 – 1025°C. Like other duplex grades 2507 has low hot strength, so may need support during heat treatment or forging. Hot forging should be followed by solution treatment.

Typical Applications

Oil and gas exploration, processing and support systems, pollution control including flue gas desulphurisation, marine and other high chloride environments, desalination plants, chemical processing, transport and storage, pulp and paper processing.

Specified Properties of Super duplex Stainless Steel grades 2507

These properties are specified for flat rolled product (plate, sheet and coil) in ASTM A240M and for pipe in ASTM A790M, as UNS S32750. Similar but not necessarily identical properties are specified for other products in their respective specifications.